E-Z WELD – Orange, Heavy Body, CPVC Cement 786 For Use On Pipes 120/240/475/947ml

E-Z Weld Heavy Body Orange is a heavy bodied, slow set CPVC Solvent Cement. This cement is part of our Industrial Grade line of products. This cement is formulated for use on CPVC pipes and fittings. It is viscous (thick) and, carries very good gap filling properties. This cement is ideal for joining large diameter CPVC pipes & fittings where the gap between pipes and fittings is large. It may also be used on small diameter pipes and fittings. This cement requires a longer cure time. When joining large diameter pipe & fittings the use of primers is highly recommended.

Application:
This cement is good for joining Schedule 40 & 80 PVC pipes and
fittings up to 12” (315 mm) diameter interference fit. It is approved for
hot (up to 180°F/82°C) and cold water pressure applications. It may
also be used for non-pressure applications such as drain, waste, vent,
sewer, gas, conduit, etc. For superior joint use with one of our E-Z
Weld Primers, Purple (212 or 221*) or Clear (211 or 224*). Never add
thinner or additive. Never use the cement if it is stringy or jelly-like.
Always follow instructions on the label.
Application temperature: 32°F to 110°F (0°C to 43°C).
Storage temperature: 45°F to 110°F (7°C to 43°C).
The ASTM has developed the following schedule and may be used
as a guide (for relative humidity 60% or less. Sch. 40 size pipe.) eg.
a 2” pipe size joint made at 55°F, 50% Relative Humidity, and a test
pressure of 100 psi would require a cure time of 4 hrs.
Certification:
This product is tested, certified and listed by NSF International for
use on drain, waste and potable water systems. It is also listed by
the International Association of Plumbing & Mechanical Ocials
(IAPMO). It carries the Uniform Plumbing Code (UPC) seal. This
cement meets ASTM Standard F493 and D2846.
Quality Assurance:
Every batch of cement is carefully checked and monitored to assure
consistently high quality standards. Records of every batch are kept. All
ingredients are purchased from approved suppliers. This cement has
passed the following test (performed in accordance with ASTM Std. F493):
Hydrostatic Burst:
• 400 psi (2.76 Mpa) after 2-hour cure time at 73°F (23°C)
• 200 psi (1.38 Mpa) after 2-hour cure time at 180°F (82°C)